EN AW-5083 1,5 x 1000 x 2000 mm
Material id:
1000181
Tloušťka
1,5 mm
Šířka
1000 mm
Délka
2000 mm
Tempr
H111
Weight
≈ 7.98 kg/pc
CO2e (avg)
≈ 7.0 kg/kg
Stock
Stock material
EN AW-5083
Je odolná vůči mořské vodě, má průměrnou pevnost, vysokou odolnost vůči korozi a je vhodná ke svařování. Její vlastnosti pro eloxování jsou průměrné.
We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.
Technical Specifications
Slitiny
| Hustota | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Název | g/cm3 | Max | Max | Max | Min | Max | Min | Max | Min | Max | Max | Max | Max | Rest |
| EN AW-5083 | 2,66 | 0.4 | 0.4 | 0.1 | 0.4 | 1 | 4 | 4.9 | 0.05 | 0.25 | 0.25 | 0.15 | 0.15 | Al |
Hliník Vlastnosti
| Tepelná vodivost | Koeficient tepelné roztažnosti | Teplota tavení | Modul elasticity | Elektrická vodivost | |||
|---|---|---|---|---|---|---|---|
| Slitina | Stav | W/m*K | µm/(m*K) | min °C | KN/mm2 | %IACS | |
| EN AW-5083 | Hx2 | 117 | 23,8 | 580 | 640 | 71 | 28,5 |
| EN AW-5083 | Hx4 | 117 | 23,8 | 580 | 640 | 71 | 28,5 |
| EN AW-5083 | Hx6 | 117 | 23,8 | 580 | 640 | 71 | 28,5 |
| EN AW-5083 | Hx8 | 117 | 23,8 | 580 | 640 | 71 | 28,5 |
| EN AW-5083 | Hx9 | 23,8 | 580 | 640 | 71 | ||
| EN AW-5083 | O | 117 | 23,8 | 580 | 640 | 71 | 28,5 |
Mechanické vlastnosti
| Rozměry | Pevnost v tahu (Rm) MPa | Mez kluzu (Rp0,2) | Tažnost | vrdost dle Brinella | Tloušťka | Tažnost A50 | Poloměr ohybu 90° | Poloměr ohybu 180° | |||||
|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Norm | Slitina | Stav | Max | Rm N/mm2 | MPa | % min | HBS | mm | % min | t | t | ||
| EN 755-2:2013 | EN AW-5083 | H111 | 200 | 270 | - | 110 | 12 | 70 | - | - | 10 | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 275 | 350 | 125 | - | 75 | 0.2 | 0.5 | 11 | 0.5 | 1 |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 275 | 350 | 125 | - | 75 | 0.5 | 1.5 | 12 | 1 | 1 |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 275 | 350 | 125 | - | 75 | 1.5 | 3 | 13 | 1 | 1.5 |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 275 | 350 | 125 | - | 75 | 3 | 6.3 | 15 | 1.5 | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 270 | 345 | 115 | - | 75 | 6.3 | 12.5 | 16 | 2.5 | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 270 | 345 | 115 | 15 | 75 | 12.5 | 50 | - | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 270 | 345 | 115 | 14 | 73 | 50 | 80 | - | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 260 | - | 110 | 12 | 70 | 80 | 120 | - | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 255 | - | 105 | 12 | 69 | 120 | 200 | - | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 250 | - | 95 | 10 | 69 | 200 | 250 | - | - | - |
| EN 485-2:2008 | EN AW-5083 | H111 | - | 245 | - | 90 | 9 | 69 | 250 | 300 | - | - | - |