EN AW-6082 150 x 20 mm
EN AW-6082
Má vysokou pevnost a je odolná vůči korozi. Slitina je vhodná ke svařování a k eloxování.
We are not liable for items out of stock. The specified weight is theoretical. Please contact us if you have any further enquiries.
Slitiny
Hustota | Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Other | |||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
Název | g/cm3 | Min | Max | Max | Max | Min | Max | Min | Max | Max | Max | Max | Max | Rest |
EN AW-6082 | 2,7 | 0.7 | 1.3 | 0.5 | 0.1 | 0.4 | 1 | 0.6 | 1.2 | 0.25 | 0.2 | 0.1 | 0.15 | Al |
Hliník Vlastnosti
Tepelná vodivost | Koeficient tepelné roztažnosti | Teplota tavení | Modul elasticity | Elektrická vodivost | |||
---|---|---|---|---|---|---|---|
Slitina | Stav | W/m*K | µm/(m*K) | min °C | KN/mm2 | %IACS | |
EN AW-6082 | O | 216 | 23,1 | 575 | 650 | 70 | 55,5 |
EN AW-6082 | T1 | 23,1 | 575 | 650 | 70 | ||
EN AW-6082 | T4 | 167 | 23,1 | 575 | 650 | 70 | 42 |
EN AW-6082 | T5 | 23,1 | 575 | 650 | 70 | ||
EN AW-6082 | T6 | 172 | 23,1 | 575 | 650 | 70 | 44 |
Mechanické vlastnosti
Rozměry | Pevnost v tahu (Rm) MPa | Mez kluzu (Rp0,2) | Tažnost | vrdost dle Brinella | Tloušťka | Tažnost A50 | Poloměr ohybu 90° | |||||
---|---|---|---|---|---|---|---|---|---|---|---|---|
Norm | Slitina | Stav | Min | Max | Rm N/mm2 | MPa | % min | HBS | mm | % min | t | |
EN 755-2:2013 | EN AW-6082 | T6 | - | 5 | 290 | 250 | 8 | 95 | - | - | 6 | - |
EN 755-2:2013 | EN AW-6082 | T6 | - | 20 | 295 | 250 | 8 | 95 | - | - | 6 | - |
EN 754-2:2013 | EN AW-6082 | T6 | - | 80 | 310 | 255 | 10 | 95 | - | - | 9 | - |
EN 755-2:2013 | EN AW-6082 | T6 | - | 5 | 290 | 250 | 8 | 95 | - | - | 6 | - |
EN 755-2:2013 | EN AW-6082 | T6 | 5 | 25 | 310 | 260 | 10 | 95 | - | - | 8 | - |
EN 755-2:2013 | EN AW-6082 | T6 | 5 | 25 | 310 | 260 | 10 | 95 | - | - | 8 | - |
EN 755-2:2013 | EN AW-6082 | T6 | 20 | 150 | 310 | 260 | 8 | 95 | - | - | - | - |
EN 755-2:2013 | EN AW-6082 | T6 | 150 | 200 | 280 | 240 | 6 | 95 | - | - | - | - |
EN 755-2:2013 | EN AW-6082 | T6 | 200 | 250 | 270 | 200 | 6 | 95 | - | - | - | - |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 310 | 260 | - | 94 | 0.4 | 1.5 | 6 | 2.5 |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 310 | 260 | - | 94 | 1.5 | 3 | 7 | 3.5 |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 310 | 260 | - | 94 | 3 | 6 | 10 | 4.5 |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 300 | 255 | - | 91 | 6 | 12.5 | 9 | 6 |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 295 | 240 | 8 | 89 | 12.5 | 60 | - | - |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 295 | 240 | 7 | 89 | 60 | 100 | - | - |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 275 | 240 | 6 | 84 | 100 | 150 | - | - |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 275 | 230 | 4 | 83 | 150 | 175 | - | - |
EN 485-2:2008 | EN AW-6082 | T6 | - | - | 260 | 220 | 2 | - | 175 | 350 | - | - |